White Tapered Top With Cylindrical Base Zirconia Ceramic Component (For High-Precision Instruments)

White Tapered Top with Cylindrical Base Zirconia Ceramic Component (For High-Precision Instruments)

Product Introduction

This product is manufactured from high-purity yttria-stabilized zirconia (Y-TZP), presenting an elegant pearl-white appearance. It features an innovative monolithic design integrating a tapered top with a cylindrical base, ensuring streamlined media guidance and providing a stable mounting reference surface. The component undergoes nano-level polishing, achieving a mirror-like finish with a surface roughness of Ra ≤ 0.1µm. This design fully leverages the unique advantages of zirconia material, including high toughness, low thermal conductivity, and exceptional wear resistance, making it specifically developed and manufactured for critical applications in high-precision instruments and fluid control systems.

Core Advantages

• Exceptional Mechanical Properties: Flexural strength ≥ 1000 MPa, fracture toughness up to 8 MPa·m¹/², 2-3 times that of conventional ceramics.

• Ultra-Low Thermal Conductivity: Thermal conductivity of 2.5 W/(m·K), effectively blocking heat transfer.

• Superior Wear Resistance: Vickers hardness HV 1300, wear rate < 1×10⁻⁷ mm³/N·m.

• Self-Lubricating特性: Friction coefficient 0.05-0.15, suitable for oil-free lubrication conditions.

• Biocompatibility: Certified per ISO 10993 for biocompatibility.

Primary Applications

• Precision Instruments: Fluid guidance components for liquid chromatographs, sample introduction systems for mass spectrometers.

• Medical Devices: Guide sleeves for dental implants, components for minimally invasive surgical instruments.

• Fluid Control: Core seats for high-precision valves, ceramic plungers for metering pumps.

• Automation Equipment: Positioning guide bushings for robotic arms, guide components for precision fixtures.

• Research Equipment: Seals for ultra-high pressure reactors, wear-resistant parts for laboratory instruments.

Specifications Table

Nanometer Zirconia Powder Preparation → Isostatic Pressing → Machining of Taper-Cylinder Structure → Vacuum Sintering at 1550°C → Hot Isostatic Pressing (HIP) → Precision CNC Grinding → Ultrasonic Cleaning → Laser Marking → Full-Dimension Inspection → Cleanroom Packaging.

Usage Instructions

1. Installation Alignment: Use dedicated installation fixtures to ensure coaxiality ≤ 0.02 mm between the tapered surface and the base.

2. Contact Surface Handling: Use PTFE gaskets as buffers at interfaces with metal components.

3. Temperature Adaptation: Avoid thermal shock; the rate of temperature change should be < 100°C/min.

4. Cleaning & Maintenance: Clean using deionized water with ultrasonic assistance; avoid scratching with hard objects.

5. Regular Inspection: Check surface wear every 1000 hours of operation.

After-Sales Service

• 24-month product quality guarantee.

• Full-process technical tracking service.

• 48-hour response for emergency orders.

• Complimentary installation technical guidance.

• Establishment of product lifecycle records.

FAQ

1. Q: What are the wear resistance advantages compared to silicon nitride?
   A: Wear resistance is improved by 40%, with service life extended by 2 times, especially under dry friction conditions.

2. Q: Do you support customization of the taper angle?
   A: Yes, taper angles from 30° to 120° are supported, with an angular accuracy of ±0.5°.

3. Q: What is the service life in strong acid environments?
   A: Can operate stably for over 10,000 hours within a pH range of 1-13.

4. Q: What is the maximum processable size range?
   A: Currently, maximum diameter is 150 mm, maximum height is 200 mm; non-standard customization is supported.

precision zirconia aluminum oxide china

unattackable ceramic and zirconia wholesaler

unattackable ceramic and zirconia distributor

White Tapered Top With Cylindrical Base Zirconia Ceramic Component (For High-Precision Instruments) Images